| Wood-based polymer Naturacell is a durable, attractive, plant-based plastic resin that can be reprocessed and reused in most applications. Best of all, it works with your existing tooling. So you can incorporate it into your products right away. Naturacell™’s extraordinary physical properties make it not only an environmentally friendly plastic, but also an ideal material for thousands of consumer products: Tough impact strength Superior clarity and transparency High surface gloss Strong chemical resistance Warm to the touch&& |
| Product Description | |
|---|---|
| Generic | CA |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good surface appearance,High impact resistance,Renewable resources,Solvent resistance,HB |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 1.4 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 to 0.60 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 2.3 to 2.6 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 120 to 260 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 65.0 to 95.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 50.0 to 87.2 | ℃ | ASTM D648 |
| Vicat Softening Temp | 90.0 to 126 | ℃ | ASTM D1525 |
| Relative temperature index | 50.0 | ℃ | UL 746 |
| Electrical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm, all colors | HB | UL 94 | |
| 3.00 mm, all colors | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 1520 µm | > 90.0 | % | ASTM D1003 |
| Haze | |||
| 1520 µm | < 8.5 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Flow Designation | H3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 96 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| yield | 66.2 | MPa | ASTM D638 |
| fracture | 66.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 15 | % | ASTM D638 |
| Bending modulus | 2160 | MPa | ASTM D790 |
| bending strength | |||
| yield | 71.7 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 66 to 71 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Barrel rear temperature | 193 to 204 | °C | |
| Barrel middle temperature | 193 to 204 | °C | |
| Barrel front temperature | 199 to 210 | °C | |
| Nozzle temperature | 210 to 221 | °C | |
| Mold temperature | 38 to 82 | °C | |
| Injection pressure | 14.5 | MPa | |
| Back pressure | 0.00 to 0.448 | MPa | |
| Vent depth | 0.051 to 0.76 | mm | |
| Melt temperature | 199 to 216 | °C | |
| Notes |
|---|
| 1. Plant-based |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |