| ACRYLITE® Resist ZK-6 polymer is an amorphous, impact-modified thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA). Typical properties of ACRYLITE® Resist acrylic polymers are: high weather resistance high light transmission improved resistance to stress cracking good melt flow rate easy to color The special properties of ACRYLITE® Resist ZK-6 polymer are: high impact/break resistance and strength low melt flow rate medium heat resistance AMECA listed as ZK6 (x) FDA food contact use Application: Used for injection molded parts and extruded sheet.&& |
| Product Description | |
|---|---|
| Supplier | ROHM |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good Clarity,High impact resistance,Good liquidity,Food contact compliance,Heat Resistance, Good,Good coloring,Amorphous |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.16 | g/cm³ | ASTM D792 |
| Apparent density | 0.71 | g/cm³ | ASTM D1895 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 1.7 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| balance | < 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 0℃，6.4mm | 37 | J/m | ASTM D256 |
| 23℃，6.4mm | 59 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 6.35 mm | 90.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 93.9 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD：0~100℃ | 7.2E-5 | 1/℃ | ASTM D696 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 3200 µm | 91.5 | % | ASTM D1003 |
| Haze | |||
| 3200 µm | 1.0 | % | ASTM D1003 |
| Yellowness index | |||
| 3.20 mm | 0.30 | YI | ASTM D1925 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 40 | ASTM D785 | |
| Tensile modulus | 1520 | MPa | ASTM D638 |
| tensile strength | 43.4 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| yield | 5.0 | % | ASTM D638 |
| fracture | 55 | % | ASTM D638 |
| Bending modulus | 1520 | MPa | ASTM D790 |
| bending strength | 59.3 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |