| ELITE™ AT 6111 Enhanced Polyethylene Resin is an ethylene-octene copolymer based on ELITE™ AT technology from Dow. This resin is designed for cast stretch machine wrap films in pallet wrap application and offers an optimized balance of extensibility, impact strength, and puncture resistance. Main Characteristics: Excellent extensibility High impact and exceptional puncture resistance Excellent processibility with low back pressure and power consumption. Complies with: U.S. FDA FCN 424 EU, No 10/2011 Canadian HPFB No Objection Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EPE |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.912 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.7 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Membrane puncture strength | |||
| 20 µm | 2.87 | J | Internal Method |
| Membrane puncture force | |||
| 20 µm | 36.9 | N | Internal Method |
| Membrane puncture resistance | |||
| 20 µm | 23.0 | J/cm³ | Internal Method |
| tensile strength | ASTM D882 | ||
| MD, yield, 20 µ m | 6.37 | MPa | ASTM D882 |
| TD, yield, 20 µ m | 6.30 | MPa | ASTM D882 |
| MD, fracture, 20 µ m | 44.3 | MPa | ASTM D882 |
| TD, fracture, 20 µ m | 38.1 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 20 µ m | 440 | % | ASTM D882 |
| TD, fracture, 20 µ m | 560 | % | ASTM D882 |
| Drop hammer impact | |||
| 20 µm | 740 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：20 µm | 240 | g | ASTM D1922 |
| TD：20 µm | 470 | g | ASTM D1922 |
| Final stretching | |||
| OnPallet Testing，20.3 µm | 300 | % | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 109 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，20.3 µm | 90 | ASTM D2457 | |
| Haze | |||
| 20.3 µm | 1.3 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B |
| 3. Determined by Highlight Industries, Inc. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |