| ICORENE® 1761 is a metallocene linear low density polyethylene for rotational moulding applications. This grade is suitable for use in general purpose applications. It has a good balance of properties such as toughness, easy flow, high impact, and surface gloss.&& |
| Product Description | |
|---|---|
| Generic | mMDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Good surface appearance,High impact resistance,High liquidity |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.935 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 6.0 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | ASTM D1693 | ||
| 10% non-ionic detergent | > 300 | hr | ASTM D1693 |
| 100% non-ionic detergent | > 1000 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-2 | ||
| yield | 18.0 | MPa | ISO 527-2 |
| fracture | 11.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 800 | % | ASTM D638 |
| Bending modulus | 700 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Falling impact resistance | |||
| -20℃ | 190 | J/cm | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 121 | ℃ | ISO 306 |
| Melting temperature | 123 | ℃ | ISO 11357 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Based on ISO 6603 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |