| About |
|---|
| This compound is designed for medical and healthcare applications requiring oil resistance.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.908 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD | 2.1 | % | |
| TD | 2.2 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 35 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| fracture | 3.28 | MPa | ASTM D412 |
| 100% strain | 0.931 | MPa | |
| 200% strain | 1.62 | MPa | |
| 300% strain | 2.45 | MPa | |
| Tensile strain | |||
| fracture | 500 | % | ASTM D412 |
| tear strength | 8.76 | kN/m | ASTM D624 |
| Compression deformation | |||
| 23℃，22 hr | 13 | % | ASTM D395 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel rear temperature | 138 to 160 | °C | |
| Barrel middle temperature | 160 to 182 | °C | |
| Barrel front temperature | 171 to 193 | °C | |
| Nozzle temperature | 193 to 216 | °C | |
| Processing (melt) temperature | 193 to 216 | °C | |
| Mold temperature | 21.1 to 37.8 | °C | |
| Injection pressure | 1.38 to 5.52 | MPa | |
| Back pressure | 0.172 to 0.689 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Barrel 1 zone temperature | 138 to 149 | °C | |
| Barrel 2 zone temperature | 149 to 160 | °C | |
| Barrel 3 zone temperature | 160 to 182 | °C | |
| Barrel 5 zone temperature | 171 to 193 | °C | |
| Nozzle temperature | 182 to 204 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |