| About |
|---|
| “Jampilen HP510L” is a polypropylene homopolymer with good flow properties and is particularly suitable for the extrusion of film yam, monofilament, cast film and sheet. “Jampilen HP510L” combines outstanding processability with good mechanical properties. Film yam made of “Jampilen HP510L” is used for baler twines, packaging twines and ropes. “Jampilen HP510L” is well suited for the production of monofilament used for instance in brush and broom filling and technical applications. Features: Good processability Good mechanical properties Homopolymer Typical Applications: Baler twines, packaging twines and ropes Brush and broom filling and technical applications Coextruded film for packaging Thin sheet for stationery folders Sheet for thermoforming Straws Gunnies&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good liquidity,Homopolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 6.0 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 40 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 94.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 154 | ℃ | ASTM D1525 2 |
| Accelerate oven aging | |||
| 150℃ | 360 | hr | ASTM D3012 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 | |
| tensile strength | |||
| yield | 35.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 12 | % | ASTM D638 |
| Bending modulus | 1500 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |