| Ultramid 8200 HS is a heat stabilized, medium viscosity, PA6 injection molding homopolymer, exhibiting resistance to sink-mark formation in thick sections, and improved toughness over conventional lower viscosity grades. It possesses a combination of strength, stiffness and toughness properties as well as excellent heat, chemical and abrasion resistance. It is available in natural and pigmented versions. Applications Ultramid 8200 HS is generally receommended for application such as wiring devices, plugs, receptacles, gears, connectors, convoluted tubing, filter housings, hinges, and textile components.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High Heat Resistance,Good wear resistance,Solvent resistance,Heat Stabilized,Homopolymer,V-2 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.2 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 9.5 | % | ISO 62 |
| saturated | 9.5 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 2.7 | % | ISO 62 |
| Balance, 50% RH | 2.7 | % | ASTM D570 |
| 24hr | 1.6 | % | ASTM D570 |
| 23℃，24hr | 1.6 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.5 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | No Break | ISO 179 | |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃ | 48 | J/m | ASTM D256 |
| 23℃ | 65 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 65.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 60.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 175 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 150 | ℃ | ISO 75-2/B |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| MD | 8.3E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| 0.71 mm | 130 | ℃ | UL 746 |
| 1.3 mm | 130 | ℃ | UL 746 |
| 3.0 mm | 130 | ℃ | UL 746 |
| 6.0 mm | 130 | ℃ | UL 746 |
| Strength mechanical performance | UL 746 | ||
| 0.71 mm | 95.0 | ℃ | UL 746 |
| 1.3 mm | 105 | ℃ | UL 746 |
| Impact mechanical performance | UL 746 | ||
| 3.0 mm | 105 | ℃ | UL 746 |
| 6.0 mm | 105 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 3.00 mm | V-2 | UL 94 | |
| 6.00 mm | V-2 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2700 | MPa | ISO 527-2 |
| tensile strength | ASTM D638 | ||
| Yield, -40 ℃ | 136 | MPa | ASTM D638 |
| Yield, 23 ℃ | 85.0 | MPa | ASTM D638 |
| Yield, 121 ℃ | 23.0 | MPa | ASTM D638 |
| tensile strength | ISO 527-2 | ||
| Yield, -40 ℃ | 136 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 80.0 | MPa | ISO 527-2 |
| Yield, 120 ℃ | 23.0 | MPa | ISO 527-2 |
| Tensile strain | ASTM D638 | ||
| Yield, 23 ℃ | 5.0 | % | ISO 527-2 |
| Yield, -40 ℃ | 3.0 | % | ASTM D638 |
| Yield, 23 ℃ | 20 | % | ASTM D638 |
| Yield, 121 ℃ | 15 | % | ASTM D638 |
| Nominal tensile fracture strain | ISO 527-2 | ||
| -40℃ | 8.0 | % | ISO 527-2 |
| 23℃ | 25 | % | ISO 527-2 |
| 120℃ | > 100 | % | ISO 527-2 |
| Bending modulus | ASTM D790 | ||
| 23℃ | 2400 | MPa | ISO 178 |
| -40℃ | 3010 | MPa | ASTM D790 |
| 23℃ | 2830 | MPa | ASTM D790 |
| 65℃ | 460 | MPa | ASTM D790 |
| 90℃ | 350 | MPa | ASTM D790 |
| 121℃ | 305 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| 23℃ | 82.0 | MPa | ISO 178 |
| -40℃ | 168 | MPa | ASTM D790 |
| 23℃ | 110 | MPa | ASTM D790 |
| 65℃ | 30.0 | MPa | ASTM D790 |
| 90℃ | 20.0 | MPa | ASTM D790 |
| 121℃ | 18.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 |
| Special value | Nominal value | Unit | Test method |
|---|---|---|---|
| Fracture, -40 ℃ | 8.0 | % | ASTM D638 |
| Fracture, 23 ℃ | 60 | % | ASTM D638 |
| Fracture, 121 ℃ | > 100 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Processing (melt) temperature | 240 to 285 | °C | |
| Mold temperature | 65 to 80 | °C | |
| Injection pressure | 3.50 to 12.5 | MPa | |
| Injection speed | Fast | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |