| About |
|---|
| Features and Benefits Composition: di-polymer of vinylidene fluoride and hexafluoropropylene Process targets: injection and transfer molding Improved scorch resistance when compared to other Dyneon FC grade products Proprietary incorporated cure technology Better mold release Better cure response to higher molding temperatures Viscosity modifier&& |
| Product Description | |
|---|---|
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Copolymer |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.80 | g/cm³ | |
| Mooney viscosity | |||
| ML 1+10，121℃ | 17 | MU | |
| Fluorine content | 66 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 75 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 13.3 | MPa | |
| 100% strain | 5.52 | MPa | |
| Tensile strain | |||
| fracture | 210 | % | |
| Compression deformation | |||
| 200℃，70 hr | 21 | % | ASTM D395B |
| MH（177℃） | 1.76 | J | |
| ML（177℃） | 0.0339 | J | |
| t’50（177℃） | 3.0 | min | |
| t’90（177℃） | 4.2 | min | |
| ts2（177℃） | 2.7 | min |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Tr10 | -18 | ℃ | ASTM D1329 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |