| About |
|---|
| TYPE: Utomer UT10P85A TPU is a BSA Polyether-type thermoplastic polyurethane (TPU) Features: Excellent clarity and UV stable with good melt strength. Uses: Extrusion for film or Compunding.&& |
| Product Description | |
|---|---|
| Supplier | Utomer |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good Clarity,Good melt strength |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | 20 to 40 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 82 to 88 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| 100% strain | > 5.00 | MPa | ASTM D412 |
| 300% strain | > 12.0 | MPa | ASTM D412 |
| tensile strength | > 30.0 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | > 800 | % | ASTM D412 |
| tear strength | > 0.0900 | kN/m | ASTM D624 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -20.0 | ℃ | ASTM D3418 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Barrel 1 zone temperature | 175 | °C | |
| Barrel 2 zone temperature | 185 | °C | |
| Barrel 3 zone temperature | 190 | °C | |
| Barrel 4 zone temperature | 195 | °C | |
| Connector temperature | 200 | °C | |
| Nozzle temperature | 195 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |