| About |
|---|
| Bayflex 110-35 IMR system produces a solid urethane elastomer which has a flexural modulus of approximately 33,500 psi* at room temperature. This system is used to provide multiple releases of large reaction injection molding (RIM) parts, such as automotive fascias. The system contains internal mold release (IMR) and is used with milled glass fiber or mineral reinforcements. Bayflex 110-35 IMR is a formulated RIM system supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. As with any product, use of the Bayflex 110-35 IMR system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PUR-脂肪族+MDI |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ASTM D792 , ASTM D1622 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.70 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | ASTM D790 | ||
| -30℃，3.18 mm | 1900 | MPa | ASTM D790 |
| 23℃，3.18 mm | 1030 | MPa | ASTM D790 |
| 65℃，3.18 mm | 689 | MPa | ASTM D790 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 3.18 mm | 22.1 | MPa | ASTM D638 |
| Fracture, 3.18 mm | 22.1 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 3.18 mm | 75 | % | ASTM D638 |
| Fracture, 3.18 mm | 75 | % | ASTM D412 |
| tear strength | |||
| 3.18 mm | 105 | kN/m | ASTM D624 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 160 | J/m | ASTM D256 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat Sag（6 in Overhang，121℃，3.18 mm） | 4.06 | mm | ASTM D3769 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD：3.2 mm | 5.0E-5 | 1/℃ | ASTM D696 |
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 53 | ||
| Component B | 按重量计算的混合比: 100 | ||
| stripping time | 0.50 | min |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 105 Index |
| 4. 1 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |