| NANCAR® 1082 is a medium high acrylonitrile rubber included with 50 phr of Di(2-ethylhexyl)phthalate (DEHP). NANCAR® 1082 can be considered as a plasticizer master batch with are used in conjunction with standard NANCAR NBR and other rubbers where the needs demand. It offers outstanding processing characteristics with the advantages of better dispersion, low power consumption and time savings especially for low durometer NBR products. NANCAR® 1082 is recommended for use in soft rollers, high extending and low durometer items.&& |
| Product Description | |
|---|---|
| Supplier | Nantex |
| Generic | NBR |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Machinable,Low Hardness,Plasticizing |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Mooney viscosity | |||
| ML 1+4，100℃ | 45 | MU | ASTM D1646 |
| Acrylonitrile content (Bound) | 31.5 | % | Internal Method |
| Stabilizer | Non-staining | ||
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 50 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 13.7 | MPa | ASTM D412 |
| 300% strain | 8.04 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 500 | % | ASTM D412 |
| Compression deformation | |||
| 100℃，70 hr | 30 | % | ASTM D395 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 100℃，70 hr | -5.0 | % | ASTM D865 |
| The rate of change in ultimate elongation in air | |||
| 100℃，70 hr | -35 | % | ASTM D865 |
| The rate of change in hardness of a hardness tester in the air | |||
| Shore A, 100 ℃, 70 hr | 5.0 | ASTM D865 | |
| The rate of change in tensile strength | ASTM D471 | ||
| 100 ℃, 70 hr, in ASTM # 1 oil | 14 | % | ASTM D471 |
| 100 ℃, 70 hr, in ASTM # 3 oil | 13 | % | ASTM D471 |
| Change rate of ultimate elongation | ASTM D471 | ||
| 100 ℃, 70 hr, in ASTM # 1 oil | -32 | % | ASTM D471 |
| 100 ℃, 70 hr, in ASTM # 3 oil | -22 | % | ASTM D471 |
| The rate of change in Shore hardness | ASTM D471 | ||
| Support A, 100 ℃, 70 hr, in ASTM # 1 oil | 20 | ASTM D471 | |
| Support A, 100 ℃, 70 hr, in ASTM # 3 oil | 10 | ASTM D471 | |
| Volume change | ASTM D471 | ||
| 100 ℃, 70 hr, ASTM standard oil (No.1) | -22 | % | ASTM D471 |
| 100 ℃, 70 hr, ASTM standard oil (No.3) | -8.0 | % | ASTM D471 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Cured for 6.00 min at 320°F |
| 3. Cured for 6.00 min at 160°C |
| 4. Cured for 11.0 min at 160°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |