| LITAC-A® 120PCF is an Acrylonitrile Styrene Copolymer (AS) material. It is available in Asia Pacific or North America for injection molding. Important attributes of LITAC-A® 120PCF are: Flame Rated High Flow&& |
| Product Description | |
|---|---|
| Supplier | Nippon |
| Generic | SAN |
| Material Status | Commercial: Active |
| Features | High liquidity,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃，10 kg | 25.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.20 to 0.50 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 1.5 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 85.0 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 6.0E-5 | 1/℃ | JIS K7197 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 127 | ISO 2039-2 | |
| tensile strength | |||
| Fracture, 23 ℃ | 69.0 | MPa | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 3600 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 121 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | > 3.0 | hr | |
| Barrel rear temperature | 210 to 250 | °C | |
| Barrel middle temperature | 210 to 250 | °C | |
| Barrel front temperature | 210 to 250 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |