| About |
|---|
| FOZEAS® J9501E50 is a Polylactic Acid (PLA) material. It is available in Asia Pacific for extrusion. Important attributes of FOZEAS® J9501E50 are: Eco-Friendly/Green Good Processability&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Renewable resources |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | JIS K7112 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.20 | g/10min | JIS K7210 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 50.0 | MPa | JIS K7161 |
| Tensile strain | |||
| fracture | 140 | % | JIS K7161 |
| Bending modulus | 3000 | MPa | JIS K7171 |
| bending strength | 75.0 | MPa | JIS K7171 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 10 | kJ/m² | JIS K7110 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 90.0 | ℃ | JIS K7191-1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |