| Talc filled compounded polypropylene produced for automotive interior applications using Mytex® Technology. This maierial exhibits high flow and good processability characteristics.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High liquidity |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 18 | g/10min | ASTM D1238 |
| Ash Content | 25 | % | ASTM D5630 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 35 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 110 | ℃ | ISO 75-2/B |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 60 | ISO 868 | |
| tensile strength | |||
| yield | 20.0 | MPa | ISO 527-2/50 |
| Bending modulus | |||
| tangent | 2170 | MPa | ISO 178 |
| Notes |
|---|
| 1. REV. K |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |