| About |
|---|
| Ixef® 3012 is a carbon-fiber and glass fiber reinforced polyarylamide compound which exhibits extremely high strength and stiffness, good surface gloss, excellent creep resistance, and lower density than glass-fiber reinforced engineering resins. Ixef® 3012 is also electrically conductive. Testing was conducted on samples dry as molded and samples conditioned to 50% relative humidity in accordance with ISO 1110-1995 E Method 4.1. Black: Ixef® 3012 BK 001&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | Paraformaldehyde |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good surface appearance,Good Dimensional Stability,High liquidity,Solvent resistance,Low moisture absorption,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.57 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 24hr | 0.24 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 38500 | MPa | ISO 527-2 |
| tensile strength | 290 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 1.1 | % | ISO 527-2 |
| Bending modulus | 36000 | MPa | ISO 178 |
| bending strength | 440 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40 ℃, completely fractured | 6.4 | kJ/m² | ISO 179 |
| -30 ℃, completely fractured | 6.4 | kJ/m² | ISO 179 |
| 23 ℃, completely fractured | 6.7 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -40 ℃, completely fractured | 50 | kJ/m² | ISO 179 |
| -30 ℃, completely fractured | 50 | kJ/m² | ISO 179 |
| 23 ℃, completely fractured | 60 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | 7.5 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | 45 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 230 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| TD | ISO 11359-2 | ||
| MD | ISO 11359-2 | ||
| 0 to 80 ℃ | 4.0E-6 | cm/cm/℃ | ISO 11359-2 |
| 130 to 200 ℃ | 2.2E-6 | cm/cm/℃ | ISO 11359-2 |
| 0 to 50 ℃ | 4.3E-5 | cm/cm/℃ | ISO 11359-2 |
| 100 to 150 ℃ | 9.0E-5 | cm/cm/℃ | ISO 11359-2 |
| 150 to 200 ℃ | 1.0E-4 | cm/cm/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Moisture content | |||
| Saturation 50% RH | — | % |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 0.50 to 1.5 | hr | |
| Barrel rear temperature | 250 to 260 | °C | |
| Barrel front temperature | 260 to 290 | °C | |
| Processing (melt) temperature | 280 | °C | |
| Mold temperature | 120 to 160 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A |
| 3. These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |