| About |
|---|
| CALIBRE™ 300V-15 系列聚碳酸酯树脂具有特别优异的抗冲击性能、耐热畸变性能和光学透明度，达到了UL94 V-2 阻燃等级。CALIBRE 300V 系列产品有两种添加剂类型的产品： CALIBRE 302V：含紫外线稳定剂。CALIBRE 303V：含脱模剂和紫外线稳定剂 政府和业界标准： CSA (加拿大标准协会) UL (美国安全检测实验室) 应用领域： 电子元器件 照明 存储介质外壳&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,V-2 |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Density | 1.2 | g/cm³ | ISO 1183-2 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 12.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ISO 527-2/50 |
| Tensile modulus | 2300 | MPa | ISO 527-2 2 |
| tensile strength | |||
| fracture | 71.0 | MPa | ISO 527-2/50 |
| yield | 60.0 | MPa | ISO 527-2 2 |
| yield | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 150 | % | ISO 527-2/50 |
| yield | 6.0 | % | ISO 527-2/50 |
| yield | 6.0 | % | ISO 527-2 2 |
| Nominal strain at break | > 50 | % | ISO 527-2 2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 97.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 25 | kJ/m² | ISO 179/1eA |
| 23℃ | 80.0 | kJ/m² | ISO 179/1eA 2 |
| -30℃ | 12.0 | kJ/m² | ISO 179/1eA 2 |
| Charpy impact strength | |||
| 23℃ | No Break | ISO 179/1eU 2 | |
| -30℃ | No Break | ISO 179/1eU 2 | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 850 | J/m | ISO 180-4A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 137 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 121 | ℃ | ISO 75-2/A |
| 1.8 MPa | 130 | ℃ | ISO 75-2 2 |
| 0.45 MPa, annealed | 140 | ℃ | ISO 75-2/B |
| 0.45 MPa | 144 | ℃ | ISO 75-2 2 |
| Vicat Softening Temp | |||
| B50 | 145 | ℃ | ISO 306 |
| B50 | 148 | ℃ | ISO 306 2 |
| Ball pressure temperature | 125 | ℃ | IEC 60335-1 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ISO 11359-2 2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 2 |
| Dielectric strength | 17 | kV/mm | IEC 60243-1 2 |
| Relative permittivity | |||
| 100 Hz | 3.00 | IEC 60250 2 | |
| 1 MHz | 3.00 | IEC 60250 2 | |
| Dissipation factor | |||
| 100 Hz | 1.0E-3 | IEC 60250 2 | |
| 1 MHz | 2.0E-3 | IEC 60250 2 | |
| Compared to the leakage tracing index | |||
| 2.00 mm, solution A | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.20 mm | V-2 | UL 94 | |
| Flame retardant level | |||
| 1.60 mm | V-2 | ISO 1210 2 | |
| Flame retardant level | |||
| 3.20 mm | V-2 | ISO 1210 2 | |
| Oxygen index | 26 | % | ISO 4589-2 2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |