| 聚碳酸酯#防弹胶，特性：低粘度，易脱模用，适合通用制品和注塑吹塑制品 |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Good stripping performance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Water absorption rate | |||
| 23℃，24hr | 0.15 | % | ASTM D570 |
| Density | |||
| 24 hrs | 1.2 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 120 | R 级 | ASTM D785 |
| Tensile strain | |||
| 23℃ | 110 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2300 | MPa | ASTM D790 |
| tensile strength | |||
| 23℃ | 60.8 | MPa | ASTM D638 |
| bending strength | |||
| 23℃ | 88.2 | MPa | ASTM D790 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric loss factor | |||
| 10Hz | 0.0092 | ASTM D-150 | |
| Surface resistivity | >10 | ohms/sq | ASTM D257 |
| Volume resistivity | 4-0 | ohms·cm | ASTM D257 |
| Dielectric constant | |||
| 10 Hz | 25.2 | PF/m | ASTM D150 |
| Dielectric strength | 16E+5 | kV/mm | ASTM D149 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | V-2 | UL 94 | |
| Hot deformation temperature | |||
| 0.455 KPa | 145 | ℃ | ASTM D648 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2m | 880 | J/m | ASTM D-256 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |