| Description: E1009L is a hot emulsion styrene-butadiene copolymer, slightly cross-linked with divinylbenzene. It is polymerized using fatty acid as emulsifier, coagulated with salt acid and stabilized with a non-staining antioxidant. Applications: E1009L is a lower gel version of the e1009h it also reduces mill shrinkage and swelling in molding improving dimensional stability and outstanding surface texture of finished products. It is also widely used in sealants and adhesives giving good balance between adhesive and cohesive properties.&& |
| Product Description | |
|---|---|
| Generic | SBR-乳液聚合 |
| Material Status | Commercial: Active |
| Features | The fouling resistance,Crosslinked,Low speed solidification point,Good bond,Inoxidizability,Copolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Mooney viscosity | |||
| ML 1+4，100℃ | 85 | MU | ASTM D1646 |
| Organic Acid | 4.0 to 6.0 | % | ASTM D5774 |
| Soap | < 0.50 | % | ASTM D5774 |
| styrene content | |||
| Bound | 23 to 25 | % | ASTM D5775 |
| Ash Content | < 1.0 | % | ASTM D5667 |
| Volatiles | < 1.0 | % | ASTM D5668 |
| Solution viscosity | |||
| 4% toluene | 290 to 370 | mPa·s | |
| Shrinkage rate | |||
| Mill | 15 to 35 | % | ASTM D1917 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Compound |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |