LEXAN™ EXL1036 resin

About
LEXAN™树脂EXL1036是一种无定形的，UV稳定的聚碳酸酯 – 硅氧烷共聚物。提供高粘度，高度稳定的机械，电气，光学和热性能。提供良好的低温（-60°C）延展性和出色的加工性能作为保护层，具有优异的挤出加工特性。良好的抗冲击性，出色的尺寸稳定性和清晰度。通过共挤出和片材挤出加工。

Product Description
Supplier	SABIC
Generic	Polycarbonate
Material Status	Commercial: Active
Features	Excellent Processability,Low temperature ductility
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, Type I, 50 mm/min	59	MPa	ASTM D638
tensile strength
Fracture, Type I, 50 mm/min	66	MPa	ASTM D638
Tensile strain
Yield, Type I, 50 mm/min	6	%	ASTM D638
Tensile strain
Fracture, Type I, 50 mm/min	130	%	ASTM D638
bending strength
Yield, 50 mm span	87.309	MPa	ASTM D790
Bending modulus
2 mm/mim	1960	MPa	ISO 178
1.3 mm/min，50mm跨距	2099.34	MPa	ASTM D790
tensile strength
Fracture, 50 mm/min	66	MPa	ISO 527
Yield, 50 mm/min	57	MPa	ISO 527
Tensile strain
Fracture, 50 mm/min	120	%	ISO 527
Yield, 50 mm/min	6	%	ISO 527
Tensile modulus
50 mm/min	2118.96	MPa	ASTM D638
1 mm/min	2070	MPa	ISO 527
bending strength
Yield, 2 mm/min	80	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	813.4	J/m	ASTM D256
Impact strength of cantilever beam notch
-30℃	676.2	J/m	ASTM D256
Total energy of instrument impact
23℃	530	cm-kgf	ASTM D 3763
Notched impact strength of cantilever beam
23℃，80103	NB	kJ/m²	ISO 180-1U
Notched impact strength of cantilever beam
-30℃，80103	NB	kJ/m²	ISO 180-1U
Impact strength of cantilever beam notch
23℃，80103	70	kJ/m²	ISO 180-1A
Impact strength of cantilever beam notch
-30℃，80103	55	kJ/m²	ISO 180-1A
Charpy Notched Impact Strength
23 ℃, 80 * 10 * 3, 62mm span	75	kJ/m²	ISO 179/1eA
-30 ℃, 80 * 10 * 3, 62mm span	60	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23 ℃, 80 * 10 * 3, 62 mm span	NB	kJ/m²	ISO 179/1eU
-30 ℃, 80 * 10 * 3, 62 mm span	NB	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	143	℃	ASTM D1525
Hot deformation temperature
1.8 MPa, 64 mm span	125	℃	ISO 75/Af
1.8 MPa, unannealed, 3.2 mm	121	℃	ASTM D648
Linear coefficient of thermal expansion
TD：23~80℃	7.2E-05	1/℃	ISO 11359-2
TD：-40~40℃	6.66E-05	1/℃	ASTM E831
MD：23~80℃	7.2E-05	1/℃	ISO 11359-2
MD：-40~40℃	6.66E-05	1/℃	ASTM E831
Vicat Softening Temp	143	℃	ISO 306
Vicat Softening Temp	141	℃	ISO 306

PHYSICAL	Nominal value	Unit	Test method
Density	1.2		ASTM D792
Shrinkage rate
MD：3.2 mm	0.4 – 0.8	%	Internal Method
Melt Flow Rate
300℃，1.20kg	5.5	g/10min	ASTM D1238
Density	1.2	g/cm³	ISO 1183
Water absorption rate
23℃，50% RH	0.15	%	ISO 62
Saturation, 23 ℃	0.35	%	ISO 62
Melt Volume Rate
300℃，1.2 kg	5	cm³/10min	ISO 1133

Process Conditions
sheet extrusion	Nominal value	Unit	Test method
Drying temperature	110 – 120	°C
Drying time	3 – 4	hrs
Drying time (cumulative)	48	hrs
Maximum water content	0.02	%
Melt temperature	245 – 260	°C
Barrel – Zone 1 Temperature	250 – 290	°C
Barrel – Zone 2 Temperature	245 – 270	°C
Barrel – Zone 3 Temperature	225 – 255	°C
Adapter temperature	225 – 255	°C
Mold temperature	240 – 260	°C
Roll stack temperature – top	75 – 115	°C
Roll stack temperature – middle	80 – 125	°C
Roll stack temperature – bottom	120 – 145	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.