| INNOPOL® CS 2-2110 is a 10% talc-filled compound based on polypropylene block-copolymer. This grade is available in nature and custom coloured form. INNOPOL® CS 2-2110 is developed for producing injection moulded automotive components.&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Negative |
| Features | Block Copolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.970 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 21 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 30.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.5 | % | ISO 527-2/50 |
| Bending modulus | 2100 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 3.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 120 | ℃ | ISO 75-2/B |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 | hr | |
| Recommended maximum moisture content | 0.070 | % | |
| Barrel rear temperature | 190 to 240 | °C | |
| Barrel middle temperature | 190 to 240 | °C | |
| Barrel front temperature | 190 to 240 | °C | |
| Processing (melt) temperature | 210 to 250 | °C | |
| Mold temperature | 10 to 50 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |