| Nexxstar 00328 is an LDPE grade, which offers good film rigidity combined with very good optical properties.&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 to 2.4 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Self dynamic, blow molded film | > 0.50 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| tensile strength | ISO 527-3 | ||
| fracture | 14.0 | MPa | ISO 527-2 |
| MD, yield, 30 µ m, blow molded film | 10.0 | MPa | |
| TD, yield, 30 µ m, blow molded film | 10.0 | MPa | |
| MD, 30 µ m, blow molded film | 29.0 | MPa | |
| TD, 30 µ m, blow molded film | 20.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| fracture | 500 | % | ISO 527-2 |
| MD:断裂, 30 µm, 吹塑薄膜 | 200 | % | |
| TD, fracture, 30 µ m, blow molded film | 550 | % | |
| Drop hammer impact | |||
| 30 µ m, blow molded film | 90 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 30 µ m, blow molded film | 3.0 | N | |
| TD: 30 µ m, blow molded film | 1.3 | N |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 91.0 to 92.0 | ℃ | ISO 306/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric strength | > 22 | kV/mm | EN 60243-1 |
| Dielectric constant | |||
| 1 MHz | 2.30 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 3.0E-4 | ASTM D150 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 30 µ m, blow molded film | 60 | ASTM D2457 | |
| Haze | |||
| 30 µ m, blow molded film | 8.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 130 | °C | |
| Barrel 2 zone temperature | 150 | °C | |
| Barrel 3 zone temperature | 180 | °C | |
| Barrel 4 zone temperature | 200 | °C | |
| Connector temperature | 220 | °C | |
| Melt temperature | 150 to 180 | °C | |
| Nozzle temperature | 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Value reported is an estimate based on ExxonMobil’s correlation from melt flow rate data measured at other standard conditions, based on ASTM D 1238. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |