| About |
|---|
| General Purpose CoEx Heat Sealable BIAXIALLY ORIENTED POLYPROPYLENE FILM TWO SIDE SEALABLE FOR FOOD PACKAGING&& |
| Product Description | |
|---|---|
| Generic | BOPP |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| dimensional stability | |||
| TD，130℃ | < 3.0 | % | |
| MD，130℃ | < 5.0 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| dynamic | 0.20 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| tensile strength | ASTM D882 | ||
| MD, yield | 117 | MPa | ASTM D882 |
| TD, yield | 207 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 190 | % | ASTM D882 |
| TD, fracture | 70 | % | ASTM D882 |
| Water vapor transmittance | |||
| 38℃，90% RH | 5.4 | g/m²/24 hr | ASTM F1249 |
| dosage | 44.1 | m²/kg |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 85 | ASTM D2457 | |
| Haze | 2.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Heat Seal Temperature | |||
| Treated Side | 121 | ℃ | |
| Untreated side | 104 | ℃ | |
| Surface energy | 38 | dyne/cm | ASTM D2578 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 5 minuites |
| 3. 5 minutes |
| 4. Internal Method |
| 5. 1/2 sec, 30 PSI |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |