Lanufene LLF 181H

About
LANUFENE LLF 181H is a linear low density polyethylene for general purpose blown film extrusion with high mechanical properties and good process-ability. LANUFENE LLF 181H contains slip additive and anti-blocking agent. The film produced from this resin characteristically exhibits good toughness, high tensile properties, outstanding puncture resistance and good optical properties. LANUFENE LLF 181H is recommended for the manufacture of general purpose blown films such as industrial liners, food packaging and agricultural film.&&

About

LANUFENE LLF 181H is a linear low density polyethylene for general purpose blown film extrusion with high mechanical properties and good process-ability. LANUFENE LLF 181H contains slip additive and anti-blocking agent. The film produced from this resin characteristically exhibits good toughness, high tensile properties, outstanding puncture resistance and good optical properties. LANUFENE LLF 181H is recommended for the manufacture of general purpose blown films such as industrial liners, food packaging and agricultural film.&&

Product Description
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Excellent Processability,Good flexibility,Smoothness,Optical performance,High anti-blocking,Food contact compliance,Good Tensile Strength,Puncture Resistant
Availabilitys	Africa & Middle East ,Europe
Process Methods	Film extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ASTM D1505
Melt Flow Rate
190℃，21.6kg	1.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	38	µm
Secant modulus			ASTM D882
1% secant, MD: 38 µ m	220	MPa	ASTM D882
1% secant, TD: 38 µ m	260	MPa	ASTM D882
tensile strength			ASTM D882
limit	21.0	MPa	ASTM D638
MD, fracture, 38 µ m	40.0	MPa	ASTM D882
TD, fracture, 38 µ m	32.0	MPa	ASTM D882
Tensile strain			ASTM D882
fracture	700	%	ASTM D638
MD, fracture, 38 µ m	700	%	ASTM D882
TD, fracture, 38 µ m	750	%	ASTM D882
Drop hammer impact
38 µm	150	g	ASTM D1709-A

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -70.0	℃	ASTM D746
Vicat Softening Temp	99.0	℃	ASTM D1525

optical performance	Nominal value	Unit	Test method
gloss
45°，38 µm	55		ASTM D2457
Haze
38 µm	12	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	190 to 220	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.