| About |
|---|
| LUVOCOM® 1301-7896 is a Polyphenylene Sulfide (PPS) material filled with carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LUVOCOM® 1301-7896 are: Conductive ESD Protection Flame Retardant Good Stiffness Heat Resistant Typical applications include: Automotive Business/Office Goods Engineering/Industrial Parts Fabrics/Fibers Medical/Healthcare&& |
| Product Description | |
|---|---|
| Supplier | Lehmann |
| Material Status | Commercial: Active |
| Features | Conductive,Good Rigidity,Flame Characteristics,High Heat Resistance,Thermal conductivity,Low Viscosity |
| Availabilitys | Latin America,Europe,Asia Pacific,Africa & Middle East ,North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，2.16kg | 14 | g/10min | ISO 1133 |
| Shrinkage rate | 0.10 to 0.30 | % | DIN 16901 |
| Water absorption rate | |||
| 23℃，24hr | < 0.050 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 23000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 145 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 0.90 | % | ISO 527-2 |
| Bending modulus | 20000 | MPa | ISO 178 |
| bending strength | 205 | MPa | ISO 178 |
| Bending strain | 1.1 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 17 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 260 | ℃ | ISO 75-2/A |
| Continuous use temperature | 220 | ℃ | UL 746B |
| Maximum operating temperature | |||
| short-term | 240 | ℃ | |
| Vicat Softening Temp | 250 | ℃ | ISO 306/A |
| Thermal conductivity coefficient | 5.0 | W/m/K |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | < 1.0E+2 | ohms | IEC 60093 |
| insulation resistance | < 1.0E+2 | ohms | IEC 60167 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | |||
| Hot air dryer | 100 to 140 | °C | |
| Hot air dryer, B | 50 to 90 | °C | |
| Drying time | |||
| Hot air dryer | 2.0 to 4.0 | hr | |
| Hot air dryer, B | > 4.0 | hr | |
| Temperature at the rear of the barrel | 300 to 320 | °C | |
| Temperature in the middle of the barrel | 310 to 330 | °C | |
| Front temperature of material barrel | 320 to 340 | °C | |
| Nozzle temperature | 320 to 340 | °C | |
| Processing (melt) temperature | 330 | °C | |
| Mold temperature | 150 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Hot-Disk, 60x60x3 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |