| K-Resin® SBC KR52是一种丁苯共聚物(SBC)材料,。 该产品在北美洲有供货,。 K-Resin® SBC KR52的主要特性有: 良好的刚度 美观 典型应用领域包括: 电影 标签&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | SBC |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Optical performance,Good Printability |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 9.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| With oneself – dynamic | 0.25 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| 1% secant, TD | 1600 | MPa | ASTM D882 |
| 1% secant, MD | 1100 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture | 90.0 | MPa | ASTM D882 |
| TD, yield | 45.0 | MPa | ASTM D882 |
| MD, fracture | 20.0 | MPa | ASTM D882 |
| MD, yield | 30.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture | 80 | % | ASTM D882 |
| MD, fracture | 260 | % | ASTM D882 |
| Elmandorf tear strength | |||
| MD | 95 | g | ASTM D1922 |
| tear strength | |||
| TD | 75 | g | ASTM D1922 |
| Oxygen permeability | 85 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water vapor transmittance | 2.0 | g·mm/m²/atm/24 hr | ASTM F1249 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Dart impact equipped with measuring instruments | 3.00 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 60.0 | ℃ | ISO 306 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 145 | ASTM D523 | |
| Haze | 4.0 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |