| About |
|---|
| ML1710SC is a metallocene linear low density polyethylene copolymer. This metallocene grade is designed for high performance film applications requiring superior optical properties and toughness. ML1710SC is formulated with a process aid and a process stabilisation package. It does not contain slip or antiblocking additives. Film Extrusion: ML1710SC is intended for film applications requiring high performance polyethylene resins. Films produced with ML1710SC have superior clarity and higher gloss, combined with excellent toughness and sealability. ML1710SC is particularly suitable for blown stretch films containing cling additives. This grade allows rapid cling development and a higher ultimate cling level, with excellent puncture resistance and toughness. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight.&& |
| Product Description | |
|---|---|
| Supplier | Qenos |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good Clarity,Good flexibility,Good surface appearance,Low density,Copolymer,Puncture Resistant |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.917 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Secant modulus | |||
| 2% secant, MD: 50 µ m | 140 | MPa | |
| 2% secant, TD: 50 µ m | 140 | MPa | |
| tensile strength | |||
| MD, yield, 50 µ m | 11.0 | MPa | |
| TD, yield, 50 µ m | 11.0 | MPa | |
| MD, fracture, 50 µ m | 54.0 | MPa | |
| TD, fracture, 50 µ m | 54.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 50 µ m | 830 | % | |
| TD, fracture, 50 µ m | 860 | % | |
| Drop hammer impact | |||
| 50 µm | > 1500 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD：50 µm | 620 | g | |
| TD：50 µm | 670 | g |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，50 µm | 72 | ASTM D2457 | |
| Haze | |||
| 50 µm | 9.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.79 in/min |
| 3. 20 in/min |
| 4. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |