TIPELIN® 6300B

About
TIPELIN 6300B is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for blow moulding of products with high stiffness and excellent environmental stress crack resistance (ESCR). The grade contains antioxidant and acid scavenger. TIPELIN 6300B is recommended for bottles and containers up to 10 litre capacity for detergents, household chemicals and for blow moulded products for packaging of aggressive industrial chemicals bounded to UN certificates. It is suitable for corrugated pipes too TIPELIN 6300B is suitable for food contact and for manufacturing of pharmaceutical packing products. The product complies with Food Contact and Pharmaceutical Regulations.&&

About

TIPELIN 6300B is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for blow moulding of products with high stiffness and excellent environmental stress crack resistance (ESCR). The grade contains antioxidant and acid scavenger. TIPELIN 6300B is recommended for bottles and containers up to 10 litre capacity for detergents, household chemicals and for blow moulded products for packaging of aggressive industrial chemicals bounded to UN certificates. It is suitable for corrugated pipes too TIPELIN 6300B is suitable for food contact and for manufacturing of pharmaceutical packing products. The product complies with Food Contact and Pharmaceutical Regulations.&&

Product Description
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,Renewable resources,Food contact compliance,Inoxidizability,Grease resistance,Solvent resistance,Bimodal molecular weight distribution,High ESCR,Resistance to detergents
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.954	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.30	g/10min	ISO 1133
190℃，21.6kg	30	g/10min	ISO 1133
190℃，5.0kg	1.3	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)
10% non-ionic detergent, F50	700	hr	ASTM D1693B

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	65		ISO 868
tensile strength
yield	32.0	MPa	ISO 527-2
Tensile strain
fracture	1300	%	ISO 527-2
yield	11	%	ISO 527-2
Bending modulus	1550	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	9.0	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	126	℃	ISO 306/A120
Oxygen sensing time
200℃	32	min	EN 728

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	150 to 165	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.