Clearflex® H&T CLH 108

About
Clearflex H&T CLH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films obtained from Clearflex H&T CLH 108 show excellent optical properties, high fracture mechanical characteristics, together with excellent performances in automatic wrapping machines (holding force, prestretch). Main Application Clearflex H&T CLH 108 is suggested for production of very-high pre-stretch film. The combination of high mechanical properties and low gel content can allow “downgauging” for many applications. In addition to that, for its high resistance to tear propagation and to puncture, together with an outstanding holding force, Clearflex H&T CLH 108 is recommended for “critical” packaging (i.e irregular shape loads, presence of sharp edges, etc…) or loads subjected to severe mechanical stresses during transportation.&&

About

Clearflex H&T CLH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films obtained from Clearflex H&T CLH 108 show excellent optical properties, high fracture mechanical characteristics, together with excellent performances in automatic wrapping machines (holding force, prestretch). Main Application Clearflex H&T CLH 108 is suggested for production of very-high pre-stretch film. The combination of high mechanical properties and low gel content can allow “downgauging” for many applications. In addition to that, for its high resistance to tear propagation and to puncture, together with an outstanding holding force, Clearflex H&T CLH 108 is recommended for “critical” packaging (i.e irregular shape loads, presence of sharp edges, etc…) or loads subjected to severe mechanical stresses during transportation.&&

Product Description
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Optical performance,Low speed solidification point,Food contact compliance,Inoxidizability,Good Tensile Strength,Low density,Good tear strength,Octene copolymer,Copolymer,Puncture Resistant
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.919	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	2.5	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
friction coefficient
With oneself – dynamic, casting thin films	> 0.50		ISO 8295

film	Nominal value	Unit	Test method
film thickness
test	23	µm
film thickness	8 to 50µm
Tensile modulus			ISO 527-3
1% secant, MD, 23 µ m, cast thin film	140	MPa
1% secant, TD, 23 µ m, cast thin film	150	MPa
tensile strength			ISO 527-3
MD, yield, 23 µ m, blow molded film	9.00	MPa
TD, yield, 23 µ m, blow molded film	10.0	MPa
MD, fracture, 23 µ m, blow molded film	48.0	MPa
TD, fracture, 23 µ m, blow molded film	40.0	MPa
Tensile strain			ISO 527-3
MD, fracture, 23 µ m, cast thin film	600	%
TD, fracture, 23 µ m, cast thin film	800	%
Drop hammer impact
23 µ m, cast thin film	170	g	ISO 7765-1
tear strength			ISO 6383-2
MD，23 µm	130.0	kN/m
TD，23 µm	170.0	kN/m

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -70.0	℃	ASTM D746
Vicat Softening Temp	95.0	℃	ISO 306/A
Melting temperature	120	℃	Internal Method

optical performance	Nominal value	Unit	Test method
gloss
45 °, 23 µ m, cast thin film	93		ASTM D2457
Haze
23 µ m, cast thin film	0.80	%	ISO 14782

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	220 to 270	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.