| InnoPlus HD1100J and HD1600J are high density polyethylene injection molding grade. They are tailored with narrow molecular weight distribution (MWD) and high flow ability. They have optimum strength property which used for general part, auto part, toy and house ware. Typical Application: Toys, Auto parts, Household products&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High liquidity,Food contact compliance,Weight distribution,High density |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.958 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 18 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| Condition B, 25% non-ionic surfactant, F50 | Initial Break | ASTM D1693 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 39 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 116 | ℃ | ASTM D1525 3 |
| Melting peak temperature | 128 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 64 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 29.4 | MPa | ASTM D638 |
| fracture | 14.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 60 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 981 | MPa | ASTM D747 |
| Bending modulus | 1230 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 165 to 190 | °C | |
| Barrel middle temperature | 165 to 190 | °C | |
| Barrel front temperature | 165 to 190 | °C | |
| Nozzle temperature | 180 to 195 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Complete Break |
| 3. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |