| Sindustris PC SC2303 is a Polycarbonate (PC) material filled with 30% glass fiber. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PC SC2303 are: Flame Rated Chemical Resistant Good Toughness Impact Resistant Typical applications include: Electrical/Electronic Applications Housings&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Solvent resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 14 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.10 to 0.30 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 200 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 140 | ℃ | ASTM D648 |
| Relative temperature index | 80.0 | ℃ | UL 746 |
| Electrical performance | 80.0 | ℃ | UL 746 |
| Impact mechanical performance | 80.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| tensile strength | |||
| Yield, 3.20 mm | 108 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 6.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 6860 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 177 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel rear temperature | 280 to 295 | °C | |
| Barrel middle temperature | 285 to 305 | °C | |
| Barrel front temperature | 290 to 310 | °C | |
| Nozzle temperature | 290 to 305 | °C | |
| Processing (melt) temperature | 290 to 315 | °C | |
| Mold temperature | 100 to 140 | °C | |
| Back pressure | 0.981 to 3.92 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.051 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |