| ALPHALAC SG970是一种高抗冲聚苯乙烯材料,。 该产品在亚太地区、北美洲、拉丁美洲或欧洲有供货,加工方式为:注射成型。 ALPHALAC SG970的主要特性有: 阻燃/额定火焰 加工性能良好 高光泽度 ALPHALAC SG970的典型应用领域为:电气用具&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good surface appearance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 6.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.80 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃，3.2mm | 49 | J/m | ASTM D256 |
| -30℃，6.5mm | 39 | J/m | ASTM D256 |
| 23℃，3.2mm | 120 | J/m | ASTM D256 |
| 23℃，6.4mm | 98 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 83.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 93.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 91.0 | ℃ | ASTM D1525 4 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 2.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm | 35.3 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm | 50 | % | ASTM D638 |
| Yield, 3.20 mm | > 5.0 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm | 2550 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm | 53.9 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 170 to 190 | °C | |
| Barrel middle temperature | 180 to 200 | °C | |
| Barrel front temperature | 190 to 210 | °C | |
| Nozzle temperature | 190 to 220 | °C | |
| Processing (melt) temperature | 190 to 220 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Back pressure | 29.4 to 58.8 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |