| CELEX 330AD is a 30% glass fiber reinforced high flow polycarbonate resin. It is formulated with proprietary additive to improve the surface aesthetics. CELEX 330AD is designed with high flexural modulus, excellent toughness and superior processability for use in structural parts of printers, scanners, copiers as well as other business machines.&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Good surface appearance,High liquidity |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 256℃，3.80kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 to 0.30 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 3.20 mm, injection molding | 113 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 3.20 mm, injection molded | 3.5 | % | ASTM D638 |
| Bending modulus | |||
| 3.20 mm, injection molded | 7580 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 172 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 160 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm, injection molded | 130 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 250 to 255 | °C | |
| Barrel middle temperature | 255 to 260 | °C | |
| Barrel front temperature | 260 to 265 | °C | |
| Nozzle temperature | 265 to 270 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |