| About |
|---|
| Chemical abbreviation according to ISO 1043-1: PBT Moulding compound ISO 7792- PBT/PET, MGHR, 08-080N, GF20 Polybutylene terephthalate, polymer blend, 20 % glass fibre reinforced, injection molded parts with superior gloss. Flammability UL 94 HB minimum thickness 0.8 mm. Recognition by Underwriters Laboratories, USA (UL)&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Good surface appearance,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 265℃，2.16 kg | 19.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7800 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 135 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2/1A/5 |
| bending strength | |||
| 23℃ | 175 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 8.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 43 | kJ/m² | ISO 179/1eU |
| 23℃ | 43 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 195 | ℃ | ISO 75-2/A |
| 8.0 MPa, unannealed | 95.0 | ℃ | ISO 75-2/C |
| Vicat Softening Temp | |||
| B50 | 220 | ℃ | ISO 306 |
| Melting temperature | 255 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 3.5E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 29 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 4.40 | IEC 60250 | |
| 1 MHz | 4.10 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.3E-3 | IEC 60250 | |
| 1 MHz | 0.018 | IEC 60250 | |
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Extreme oxygen index | 20 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 140 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 20 to 50 | °C | |
| Barrel rear temperature | 250 to 260 | °C | |
| Barrel middle temperature | 250 to 260 | °C | |
| Barrel front temperature | 260 to 270 | °C | |
| Nozzle temperature | 265 to 275 | °C | |
| Processing (melt) temperature | 265 to 275 | °C | |
| Mold temperature | 90 to 100 | °C | |
| Injection pressure | 60.0 to 100 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 30s |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |