| About |
|---|
| Description LUTENE FB3000 is mainly intended for the extrusion of blown film with high mechanical property for the clarity bags in all thickness. LUTENE FB3000 have high mechanical property and enables the production of very thin, clear, glossy film. (LUTENE FB3000 contains slip agent and antiblock agent.) Main Applications Clarity bags in all thicknesses, film for automatic packaging, packing of textiles, lightweight carrier bags, shrink film for packing, film for lamination&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | PE |
| Material Status | Commercial: Active |
| Features | Smoothness,High anti-blocking |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | 0.080 | ASTM D1894 | |
| Tear resistance | |||
| MD：50.0 µm | 88.3 | kN/m | |
| TD：50.0 µm | 83.4 | kN/m |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| tensile strength | |||
| MD, fracture, 50 µ m | 18.6 | MPa | |
| TD, fracture, 50 µ m | 18.1 | MPa | |
| Tensile strain | |||
| MD, fracture, 50 µ m | 420 | % | |
| TD, fracture, 50 µ m | 610 | % | |
| Drop hammer impact | |||
| 50 µm | 110 | g | ASTM D1709 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 90.0 | ℃ | ASTM D1525 |
| Melting temperature | 110 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60°，50.0 µm | 95 | ASTM D2457 | |
| Haze | |||
| 50 µm | 8.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 140 to 160 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |