ACLAR® Rx20e - SOLIAO

About
Aclar® Rx20e is a 0.80 mil (20 micron) CTFE homopolymer, high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment and offers all of the benefits of Aclar® in a mid-range barrier material.&&

Product Description
Supplier	Honeywell
Generic	PCTFE
Material Status	Commercial: Active
Features	Block resin,Homopolymer
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Thermo forming

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	2.11	g/cm³	ASTM D1505

film	Nominal value	Unit	Test method
Secant modulus			ASTM D882
MD：20 µm	1400	MPa	ASTM D882
TD：20 µm	1340	MPa	ASTM D882
tensile strength			ASTM D882
MD, yield, 20 µ m	89.6	MPa	ASTM D882
TD, yield, 20 µ m	47.9	MPa	ASTM D882
Tensile strain			ASTM D882
MD, yield, 20 µ m	120	%	ASTM D882
TD, yield, 20 µ m	250	%	ASTM D882
Water vapor transmittance			ASTM F1249
20 µm，25℃，60% RH	0.039	g·mm/m²/atm/24 hr	ASTM F1249
20 µm，30℃，60% RH	0.062	g·mm/m²/atm/24 hr	ASTM F1249
20 µm，40℃，75% RH	0.26	g·mm/m²/atm/24 hr	ASTM F1249
20 µm，38℃，100% RH	0.29	g·mm/m²/atm/24 hr	ASTM F1249

THERMAL	Nominal value	Unit	Test method
Crystallization peak temperature
DSC	211	℃	ASTM D3418

optical performance	Nominal value	Unit	Test method
Haze
20.3 µm	< 1.0	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.