| Product Description | |
|---|---|
| Generic | PS (special type) |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good surface appearance,High impact resistance,HB |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 6.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23 ℃, 3.20 mm, injection molding | 32.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 3.20 mm, injection molding | 20 | % | ASTM D638 |
| Bending modulus | |||
| 23 ℃, 3.20 mm, injection molding | 2000 | MPa | ASTM D790 |
| bending strength | |||
| 23 ℃, 3.20 mm, injection molding | 50.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 40 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm, injection molded | 78.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 98.0 | ℃ | ASTM D1525 3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, 3200 µ m, injection molded film | 95 | ASTM D523 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 260 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Melt temperature | 180 to 260 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |