PRE-ELEC® TPU 1511

About
PRE-ELEC® TPU 1511 is electrically conductive polyester based thermoplastic polyurethane (TPU) compound. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® TPU 1511 has retained the excellent mechanical properties of the base elastomer. PRE-ELEC® TPU 1511 has been developed for extrusion but it can also be injection moulded. Typical applications included extruded conveyor belts, sheets and injection moulded technical parts.&&

About

PRE-ELEC® TPU 1511 is electrically conductive polyester based thermoplastic polyurethane (TPU) compound. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® TPU 1511 has retained the excellent mechanical properties of the base elastomer. PRE-ELEC® TPU 1511 has been developed for extrusion but it can also be injection moulded. Typical applications included extruded conveyor belts, sheets and injection moulded technical parts.&&

Product Description
Supplier	Premix Oy
Generic	TPU
Material Status	Commercial: Active
Features	Conductive
Availabilitys	North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.30	g/cm³	ASTM D792
Density	1.30	g/cm³	ISO 1183
Melt Flow Rate
190℃，10.0kg	2.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Shore hardness			ASTM D2240
Shaw’s A	95		ASTM D2240
Shaw’s D	52		ASTM D2240
Shore hardness			ISO 868
Shaw’s A	95		ISO 868
Shaw’s D	52		ISO 868
tensile strength	33.0	MPa	ASTM D638
yield	33.0	MPa	ASTM D638
yield	33.0	MPa	ISO 527-2
4 mm	33.0	MPa	ISO 527-2
Tensile strain
Fracture, 4 mm	> 560	%	ISO 527-2
fracture	560	%	ASTM D638
yield	530	%	ASTM D638
yield	530	%	ISO 527-2

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	< 1.0E+4	ohms	ESD STM11.11
Surface resistivity	< 1.0E+4	ohms	IEC 61340-2-3
Volume resistivity	< 5.0E+2	ohms·cm	Internal Method

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Drying temperature	80 to 100	°C
Drying time	1.0 to 2.0	hr
Processing (melt) temperature	180 to 220	°C
Mold temperature	30 to 50	°C
Injection speed	Moderate-Fast
Drying temperature	80 to 100	°C
Drying time	1.0 to 2.0	hr
Barrel 1 zone temperature	170	°C
Barrel 2 zone temperature	180	°C
Barrel 3 zone temperature	190	°C
Barrel 4 zone temperature	200	°C
Barrel 5 zone temperature	210	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.