| About |
|---|
| PC, injection molding grade&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | HB,V-2 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ISO 1133 |
| Shrinkage rate | 0.50 to 0.70 | % | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 527-2 | ||
| yield | 63.0 | MPa | ISO 527-2 |
| fracture | 58.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 70 | % | ISO 527-2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 15 | kJ/m² | ISO 180-1A |
| 23℃ | 60 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 140 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| A50 | 150 | ℃ | ISO 306/A50 |
| B50 | 144 | ℃ | ISO 306 |
| Ball pressure test | |||
| 125℃ | Pass |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | Internal Method | ||
| 3.20 mm | HB | Internal Method | |
| 0.75 mm | V-2 | Internal Method | |
| 1.60 mm | V-2 | Internal Method | |
| Glowing wire flammability index | |||
| 2.0 mm | 850 | ℃ | IEC 60695-2-12 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. UL94 internally tested |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |