| Warning: The status of this material is ‘Commercial: Limited Issue’ The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.-&& |
| Product Description | |
|---|---|
| Generic | PEEK |
| Material Status | Commercial: Negative |
| Features | Crystal,Lubricating,Solvent resistance,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.050 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.12 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 91 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 750 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 288 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 50 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 125 | ASTM D785 | |
| Tensile modulus | 27600 | MPa | ASTM D638 |
| tensile strength | 200 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.2 | % | ASTM D638 |
| Bending modulus | 17200 | MPa | ASTM D790 |
| bending strength | 296 | MPa | ASTM D790 |
| friction coefficient | ASTM D1894 | ||
| &Metal – Dynamic | 0.19 | ASTM D1894 | |
| Metal – Static | 0.17 | ASTM D1894 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 149 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 357 to 427 | °C | |
| Barrel middle temperature | 357 to 427 | °C | |
| Barrel front temperature | 357 to 427 | °C | |
| Mold temperature | 177 to 260 | °C | |
| Injection pressure | 68.9 to 103 | MPa | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Clamping force | 6.9 to 11 | kN/cm² | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |