| PTS PPE-LXS314-10 is a Polyphenylene Ether + PS (PPE+PS) product filled with 10% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Industrial Applications. Primary characteristic: impact resistant.&& |
| Product Description | |
|---|---|
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，5.0kg | 21 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.30 to 0.50 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 10 | % | ASTM D638 |
| Bending modulus | 3200 | MPa | ASTM D790 |
| bending strength | 110 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 14.0 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 120 | ℃ | ASTM D648 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. solid |
| 3. Type I |
| 4. 0.10 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |