| About |
|---|
| Jamplast Inj-03 ABS is a general injection molding grade of ABS (Acrylonitrile Butadiene Styrene). It is a high-impact, high-gloss ABS, available only in natural and black. Typical applications include housings, toys, small appliances, and cusumer goods.&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 220℃，10.0kg | 12 | g/10min | ASTM D1238 |
| 230℃，3.80kg | 5.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -40℃，3.2mm | 64 | J/m | ASTM D256 |
| 23℃，3.2mm | 380 | J/m | ASTM D256 |
| 23℃，12.7mm | 210 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 12.7 mm | 92.0 | ℃ | ASTM D648 |
| 0.45 MPa, annealed, 12.7 mm | 99.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 12.7 mm | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 12.7 mm | 94.0 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 12.7 mm, molded | 102 | ℃ | ASTM D648 |
| Vicat Softening Temp | 106 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD | 9.0E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 109 | ASTM D785 | |
| Tensile modulus | 2550 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 42.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 30 | % | ASTM D638 |
| Bending modulus | 2600 | MPa | ASTM D790 |
| bending strength | |||
| yield | 72.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 to 77 | °C | |
| Drying time | 4.0 | hr | |
| Dew Point | 29 | °C | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 235 to 249 | °C | |
| Barrel middle temperature | 241 to 254 | °C | |
| Barrel front temperature | 246 to 260 | °C | |
| Nozzle temperature | 246 to 260 | °C | |
| Processing (melt) temperature | 246 to 274 | °C | |
| Mold temperature | 43 to 66 | °C | |
| Injection pressure | 68.9 to 110 | MPa | |
| Back pressure | 0.00 to 0.172 | MPa | |
| Clamping force | 3.1 to 6.2 | kN/cm² | |
| Cushion | < 6.35 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |