| About |
|---|
| Medium melt viscosity, more suitable for extrusion molding. J-2 PVDF as raw materials, the finished products has excellent mechanical strength and flexibility. It can not be eroded by acid, alkali, strong oxidant, halogens. Good durability to aliphatic hydrocarbons, aromatic hydrocarbons, alcohol, aldehyde etc. In the work of hydrochloric acid, nitric acid, sulfuric acid, dilute alkali liquor, dense alkali liquor(40%) and 100deg.C, which keep stable. Others, J-2 PVDF finished products has the properties of gamma-Ray resistant, UV resistant, and stability in wide temperature range. Application: Be used in manufacturing PVDF tubes, PVDF pipes, PVDF rod etc.&& |
| Product Description | |
|---|---|
| Supplier | Ofluorine |
| Generic | PVDF |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good flexibility,Alkali resistant,Ethanol tolerance,Gamma radiation,Acidproof,Low odor,Inoxidizability,Heat Stabilized,Hydrocarbons,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.77 to 1.79 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，12.5kg | 10 to 25 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| balance | < 0.050 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 165 to 171 | ℃ | ASTM D3418 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 70 to 80 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| Yield, 23 ℃ | > 40.0 | MPa | ASTM D638 |
| Fracture, 23 ℃ | > 30.0 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Yield, 23 ℃ | 5.0 to 10 | % | ASTM D638 |
| Fracture, 23 ℃ | > 50 | % | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |