| About |
|---|
| Alkatane HDF895 is a medium molecular weight High Density Polyethylene grade with high stiffness and excellent moisture barrier properties. Film Extrusion: Alkatane HDF895 is particularly suitable for the production of film for the packaging of dry foods where low moisture transmission may allow extended shelf life. Numerous other applications benefit from blending Alkatane HDF895 to enhance the stiffness of LDPE / LLDPE based films, including in the core layer of high clarity coextruded films.&& |
| Product Description | |
|---|---|
| Supplier | Qenos |
| Generic | MMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.960 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 18 | µm | |
| Secant modulus | ASTM D882 | ||
| 2% secant, MD | 750 | MPa | ASTM D882 |
| 2% secant, TD | 780 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield | 24.0 | MPa | ASTM D882 |
| TD, yield | 25.0 | MPa | ASTM D882 |
| MD, fracture | 44.0 | MPa | ASTM D882 |
| TD, fracture | 29.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 680 | % | ASTM D882 |
| TD, fracture | 980 | % | ASTM D882 |
| Drop hammer impact | < 50 | g | ASTM D1709 |
| tear strength | ASTM D1922 | ||
| MD | 9.0 | cN | ASTM D1922 |
| TD | 498.0 | cN | ASTM D1922 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.79 in/min |
| 3. 2.0 in/min |
| 4. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |