| About |
|---|
| Dynaflex™ G7430-9001-00 is an easy processing, high performance compound designed for use in applications requiring tough, durable material. Excellent Heat Stability Good Ozone and UV Stability Overmold Adhesion to Polypropylene Suitable for Outdoor Use&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Renewable resources,Ozone resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 10 seconds | 68 | ASTM D2240 | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| Fracture, 23 ℃ | 8.96 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 2.48 | MPa | ASTM D412 |
| 300% Strain, 73°F | 4.07 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 23 ℃ | 650 | % | ASTM D412 |
| tear strength | 36.8 | kN/m | ASTM D624 |
| Compression deformation | |||
| 23℃，22 hr | 17 | % | ASTM D395B |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 3.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 1.8 to 2.2 | % | ASTM D955 |
| Apparent viscosity of melt | |||
| 200℃，11200 sec^-1 | 12.6 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 168 to 177 | °C | |
| Barrel middle temperature | 177 to 188 | °C | |
| Barrel front temperature | 188 to 227 | °C | |
| Nozzle temperature | 188 to 227 | °C | |
| Back pressure | 0.345 to 1.03 | MPa | |
| Screw speed | 40 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 2 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |