| BT200 is a natural, 20% mineral filled polypropylene compound intended for injection moulding and extrusion profile. BT200 has a rather low flow rate and outstanding process ability. APPLICATIONS Noise protection in industrial applications Household appliances Miscellaneous electrical components Technical components Automotive climate control parts Profiles Products requiring excellent rigidity, low shrinkage and high dimensional stability can suitably be made from BT200.&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Low liquidity,Good Dimensional Stability,Renewable resources,Low contractility,HB |
| Availabilitys | Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| Shrinkage rate | 1.1 to 1.6 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2550 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 31.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 8.0 | % | ISO 527-2/50 |
| Bending modulus | 2490 | MPa | ISO 178 |
| bending strength | 42.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 70 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 70.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 122 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 154 | ℃ | ISO 306/A |
| Ball pressure test | |||
| 125℃ | Pass | NF C 61-303 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 | hr | |
| Processing (melt) temperature | 210 to 260 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Injection speed | Moderate | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |