Celstran® PA66-GF50-0112P7,5/10

About
Material code according to ISO 1043-1: PA66 Nylon 66/6 Copolymer reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 7.5 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.&&

About

Material code according to ISO 1043-1: PA66 Nylon 66/6 Copolymer reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 7.5 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.&&

Product Description
Supplier	Celanese
Generic	PA66/6
Material Status	Commercial: Active
Features	Good Rigidity,Low warping,Good flexibility,High impact resistance,low-temperature impact resistance
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.55	g/cm³	ISO 1183

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
—	16400	MPa	ISO 527-2/1A/1
80℃	10000	MPa	ISO 527-2/1A
tensile strength
fracture	220	MPa	ISO 527-2/1A/5
80℃	140	MPa	ISO 527-2/1A
Tensile strain
fracture	1.6	%	ISO 527-2/1A/5
Fracture, 80 ℃	2.4	%	ISO 527-2/1A
Bending modulus
23℃	14000	MPa	ISO 178
bending strength			ISO 178
23℃	300	MPa	ISO 178
80℃	250	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	36	kJ/m²	ISO 179/1eA
23℃	35	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength			ISO 179/1eU
-30℃	59	kJ/m²	ISO 179/1eU
23℃	61	kJ/m²	ISO 179/1eU
Notched impact strength of cantilever beam			ISO 180/1U
-30℃	48	kJ/m²	ISO 180/1U
23℃	57	kJ/m²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	235	℃	ISO 75-2/A
8.0 MPa, unannealed	220	℃	ISO 75-2/C
Melting temperature	240	℃	ISO 11357-3

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	70 to 80	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.15	%
Hopper temperature	70 to 80	°C
Barrel rear temperature	280 to 285	°C
Barrel middle temperature	280 to 290	°C
Barrel front temperature	290 to 300	°C
Nozzle temperature	310 to 320	°C
Processing (melt) temperature	310 to 320	°C
Mold temperature	90 to 120	°C
Injection pressure	120 to 150	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
2. 10°C/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.