| Hepla® H7110GF FR is a Polyamide 6 (Nylon 6) product filled with 10% glass fiber.Characteristics include:Flame Retardant,Self- Lubricating,Impact Resistant. |
| Product Description | |
|---|---|
| Supplier | NFD |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Self-lubricating,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.53 | g/cm³ | ASTM D792 |
| water content | 0.2 | % | |
| Shrinkage rate | |||
| MD：3.20 mm | 0.4 to 0.6 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24 hrs | 1.5 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6089 | MPa | ASTM D638 |
| tensile strength | 89 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 3 to 5 | % | ASTM D638 |
| Bending modulus | 5045 | MPa | ASTM D790 |
| bending strength | 137.2 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 116 | ASTM D785 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.20 mm | 75.5 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 487 | J/m | ASTM D4812 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.5 mm | V-0 | UL 94 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | >1.0E+14 | Ohms∙cm | ASTM D257 |
| Dielectric constant | |||
| 1 MHz | 3.8 | ASTM D150 | |
| Dissipation factor | |||
| 1 MHz | 0.017 | ASTM D150 | |
| Dielectric strength | |||
| In oil | 19 | kV/mm | ASTM D149 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 199 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 182 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| Processing | Nominal value | Unit | Test method |
| Injection pressure | 68.9-103 | MPa | |
| Melt Temperature | 243-279 | ℃ | |
| Mold temperature | 54-93 | ℃ | |
| drying temperature | 82 | ℃ | |
| Drying time | 2 | hrs | |
| Dew point temperature | -18 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |