| Applications: Sheaves wheels rollers mandrel segments coupling parts vibrator parts&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Hardness,Elastic |
| Availabilitys | North America,Europe |
| Process Methods | casting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 2.2 | % | ISO 62 |
| Saturation, 23 ℃ | 7.0 | % | ISO 62 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | IEC 60093 |
| Dielectric strength | 50 | kV/mm | IEC 60243-1 |
| Dielectric constant | 3.70 | IEC 60250 | |
| Dissipation factor | 0.030 | IEC 60250 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 160 | MPa | ISO 2039-1 |
| Tensile modulus | 3700 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| yield | 85.0 | MPa | ISO 527-2 |
| fracture | 140 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 25 | % | ISO 527-2 |
| Bending modulus | 3300 | MPa | ISO 178 |
| compressive strength | ISO 604 | ||
| 5% strain | 39.0 | MPa | ISO 604 |
| 10% strain | 63.0 | MPa | ISO 604 |
| 20% strain | 90.0 | MPa | ISO 604 |
| friction coefficient | ASTM D1894 | ||
| Steel – Dynamic | 0.040 | ASTM D1894 | |
| Steel – Static | 0.35 | ASTM D1894 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | > 3.5 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | 无断裂 | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 120 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| MD：20~100℃ | 7.0E-5 to 8.0E-5 | 1/℃ | ISO 11359-2 |
| specific heat | 1670 | J/kg/℃ | ASTM C351 |
| Thermal conductivity coefficient | 0.25 | W/m/K | ISO 8302 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |