| About |
|---|
| Smart™ 151S, metallocene LLDPE, is an ethylene-octene copolymer produced via Nexlene™ technology. Smart™ 151S performs well in a wide range of various food & non- food packaging films with excellent sealing property, impact strength, and processibility. Typical Performance: Excellent low seal initiation temperature and hot tack strength Superior impact strength and transparency Outstanding bubble stability & processability Compiles with: US. FDA 21 CFR 177.1520 EU. No 10/2011 Additives: Antiblock: 2000 ppm Slip: 1000 ppm&& |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,High impact resistance,Smoothness,High anti-blocking,Food contact compliance,Low density,Octene copolymer,Copolymer,Low temperature heat sealing |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.916 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | ASTM D374 |
| Secant modulus | |||
| 1% secant, MD: 40 µ m | 143 | MPa | |
| 1% secant, TD: 40 µ m | 169 | MPa | |
| tensile strength | |||
| MD, fracture, 40 µ m | 51.0 | MPa | |
| TD, fracture, 40 µ m | 53.9 | MPa | |
| Tensile strain | |||
| MD, fracture, 40 µ m | 580 | % | |
| TD, fracture, 40 µ m | 650 | % | |
| Drop hammer impact | |||
| 40 µm | 900 | g | ASTM D1709-A |
| Elmandorf tear strength | |||
| MD：40 µm | 12 | g | |
| TD：40 µm | 22 | g |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 103 | ℃ | ASTM D1525 |
| Melting temperature | 113 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | 11 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Sealing Initial Temperature | 104 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |