| LANUFENE HDF 5116 is a high density polyethylene copolymer designed primarily for conversion into tough thin gauged blown films exhibiting high stiffness with good process-ability. LANUFENE HDF 5116 is suitable for general purpose of medium strength HDPE film applications such as bags, liners, barrier film, agricultural mulching film, Co-extrusion film, etc.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Food contact compliance,Good melt strength,High ESCR |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.951 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.15 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 16 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | > 500 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | 1130 | MPa | ASTM D790 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 15 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 15 µ m | 1400 | MPa | ASTM D882 |
| 1% secant, TD: 15 µ m | 1700 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| limit | 31.0 | MPa | ASTM D638 |
| MD, fracture, 15 µ m | 35.0 | MPa | ASTM D882 |
| TD, fracture, 15 µ m | 32.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| fracture | 800 | % | ASTM D638 |
| MD, fracture, 15 µ m | 350 | % | ASTM D882 |
| TD, fracture, 15 µ m | 500 | % | ASTM D882 |
| Drop hammer impact | |||
| 15 µm | 25 | g | ASTM D1709-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 180 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 180 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |